Title

Strengthening mechanisms in an Al-Fe-Cr-Ti nano-quasicrystalline alloy and composites

AuthorsPedrazzini, S.; Galano, M.; Audebert, F.; Collins, D.M.; Hofmann, F.; Abbey, B.; Korsunsky, A.M.; Lieblich, Marcela ; García Escorial, Asunción; Smith, G.D.
KeywordsQuasicrystals
Fibre composites
Strengthening mechanisms
Mechanical properties
Aluminium
Issue Date2016
PublisherElsevier
CitationMaterials Science & Engineering A: Structural Materials: Properties, Microstructure and Processing 672: 175-183 (2016)
AbstractWe report a study of the structure-processing-property relationships in a high strength AlFeCrTi nano-quasicrystalline alloy and composites containing 10 and 20 vol% ductilising pure Al fibres. The superimposed contributions of several different strengthening mechanisms have been modelled analytically using data obtained from systematic characterisation of the monolithic alloy bar. An observed yield strength of 544 MPa has been substantiated from a combination of solid solution strengthening, work hardening, precipitation hardening and Hall-Petch grain size dependent effects. These materials have been shown by other authors in previous published work to be highly sensitive to the size distribution of particles in the powder from which they are made, and the subsequent thermomechanical processing conditions. The processing condition employed in this study provided micron-sized grains with a strong [111] preferential orientation along the extrusion direction and a bimodal size distribution of the icosahedral nano-quasicrystalline precipitates. Both were deemed to be a significant contributor to the high yield strength observed. The addition of pure Al fibres was found to decrease the yield strength linearly with increasing Al content, and to augment the ductility of the composites.
Publisher version (URL)http://dx.doi.org/10.1016/j.msea.2016.07.007
URIhttp://hdl.handle.net/10261/143294
DOIhttp://dx.doi.org/10.1016/j.msea.2016.07.007
Identifiersdoi: 10.1016/j.msea.2016.07.007
issn: 0921-5093
Appears in Collections:(CENIM) Artículos
Files in This Item:
File Description SizeFormat 
Strengthening Mechanisms.pdf2,31 MBAdobe PDFThumbnail
View/Open
Show full item record
Review this work
 


WARNING: Items in Digital.CSIC are protected by copyright, with all rights reserved, unless otherwise indicated.