Título

Optical and Piezoelectric Study of KNN Solid Solutions Co-Doped with La-Mn and Eu-Fe

AutorPeña-Jiménez, Jesús-Alejandro; González, Federico; López-Juárez, Rigoberto; Hernández-Alcántara, José-Manuel; Camarillo, Enrique; Murrieta-Sánchez, Héctor; Pardo, Lorena ; Villafuerte-Castrejón, María-Elena
Fecha de publicación28-sep-2016
EditorMultidisciplinary Digital Publishing Institute
CitaciónMaterials 9(10): 805 (2016)
ResumenThe solid-state method was used to synthesize single phase potassium-sodium niobate (KNN) co-doped with the La<sup>3+</sup>–Mn<sup>4+</sup> and Eu<sup>3+</sup>–Fe<sup>3+</sup> ion pairs. Structural determination of all studied solid solutions was accomplished by XRD and Rietveld refinement method. Electron paramagnetic resonance (EPR) studies were performed to determine the oxidation state of paramagnetic centers. Optical spectroscopy measurements, excitation, emission and decay lifetime were carried out for each solid solution. The present study reveals that doping KNN with La<sup>3+</sup>–Mn<sup>4+</sup> and Eu<sup>3+</sup>–Fe<sup>3+</sup> at concentrations of 0.5 mol % and 1 mol %, respectively, improves the ferroelectric and piezoelectric behavior and induce the generation of optical properties in the material for potential applications.
URIhttp://hdl.handle.net/10261/142116
DOIhttp://dx.doi.org/10.3390/ma9100805
Identificadoresdoi: 10.3390/ma9100805
Aparece en las colecciones: (ICMM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
materials-09-00805.pdf10,4 MBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.