Título

High temperature oxidation resistance of (Ti,Ta)(C,N)-based cermets

AutorChicardi, E. ; Córdoba, J.M. ; Gotor, F.J.
Palabras claveA. Ceramic matrix composites
A. Cobalt
A. Titanium
B. SEM
B. X-ray diffraction
C. Oxidation
Fecha de publicación2016
EditorElsevier
CitaciónCorrosion Science, 102: 126-136(2016)
ResumenCermets based on titanium–tantalum carbonitride were oxidized in static air between 800 °C and 1100 °C for 48 h. The thermogravimetric and microstructural study showed an outstanding reduction in the oxidation of more than 90% when the Ta content was increased. In cermets with low Ta content, the formation of a thin CoO/Co3O4 outer layer tends to disappear by reacting with the underlying rutile phase, which emerges at the surface. However, in cermets with higher Ta content, the formation of an external titanate layer, observed even at a low temperature, appears to prevent the oxygen diffusion and the oxidation progression
Versión del editorhttp://dx.doi.org/10.1016/j.corsci.2015.10.001
URIhttp://hdl.handle.net/10261/130084
DOI10.1016/j.corsci.2015.10.001
Aparece en las colecciones: (ICMS) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
Datos adjuntos sin título 00031.pdf2,79 MBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 

Artículos relacionados:


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.