Título

Engineering the microstructure and magnetism of La2CoMnO6-δ thin films by tailoring oxygen stoichiometry

AutorGalceran, Regina ; Frontera Beccaria, Carlos; Balcells, Lluis ; Cisneros-Fernández, J.; López Mir, Laura ; Roqueta, Jaume ; Santiso, José ; Bagués, Núria; Bozzo, B.; Pomar, Alberto ; Sandiumenge, Felip ; Martínez Perea, Benjamín
Fecha de publicación2014
EditorAmerican Institute of Physics
CitaciónApplied Physics Letters 105(24): 242401 (2014)
ResumenWe report on the magnetic and structural properties of ferromagnetic-insulating La2CoMnO6-δ thin films grown on top of (001) SrTiO3 substrates by means of RF sputtering technique. Careful structural analysis, by using synchrotron X-ray diffraction, allows identifying two different crystallographic orientations that are closely related to oxygen stoichiometry and to the features (coercive fields and remanence) of the hysteresis loops. Both Curie temperature and magnetic hysteresis turn out to be dependent on the oxygen stoichiometry. In situ annealing conditions allow tailoring the oxygen content of the films, therefore controlling their microstructure and magnetic properties.
DescripciónUnder the terms of the Creative Commons Attribution (CC BY) license to their work.
Versión del editorhttp://dx.doi.org/10.1063/1.4904410
URIhttp://hdl.handle.net/10261/126856
DOI10.1063/1.4904410
Identificadoresdoi: 10.1063/1.4904410
issn: 0003-6951
e-issn: 1077-3118
Aparece en las colecciones: (CIN2) Artículos
(ICMAB) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
oxygen stoichiometry.pdf1,49 MBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 

Artículos relacionados:


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.