Título

Sliding wear resistance of sintered SiC-fiber bonded ceramics

AutorVera, M.C. ; Ramírez-Rico, J.; Martínez-Fernández, Julián; Singh, M.
Palabras claveSilicon carbide
Wear
Composites
Fibers
Fecha de publicación2015
EditorElsevier
CitaciónInternational Journal of Refractory and Hard Materials, 49: 232-239(2015)
ResumenAdvanced SiC-based ceramics and fiber reinforced composites are interesting materials for a wide variety of applications involving sliding wear conditions because of their excellent thermomechanical properties. The microstructure and wear resistance of sintered SiC fiber bonded ceramics (SA Tyrannohex) were studied. The material is composed of SiC-fibers in two orientations, with polygonal cross sections and cores having higher carbon content than their surroundings, as observed with SEM. A thin layer of C exists between the fibers. This layer has been found to be a turbostratic-layered structure oriented parallel to the fiber surface. XRD shows that the material is highly crystalline and composed mostly of β-SiC. Unlubricated wear behavior of the SA-Tyrannohex material when sliding against a Si3N4 ball in air at room temperature was evaluated. Experiments were performed using a pin on disk apparatus, under different normal loads of 2, 5 and 10 N at sliding speeds of 25, 50, 100 mm/s. A decrease of the friction coefficient with load was found due to the presence of the turbostratic carbon layer between the fibers. Wear rates of the order of 100 mm3/MJ were obtained, independently of sliding speed. Microfracture of the fibers is the main wear mechanism.
Versión del editorhttp://dx.doi.org/10.1016/j.ijrmhm.2014.06.020
URIhttp://hdl.handle.net/10261/121600
DOI10.1016/j.ijrmhm.2014.06.020
Aparece en las colecciones: (ICMS) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
Sliding_Wear_Final.pdf1,51 MBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 

Artículos relacionados:


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.