Modification of thermoelectric properties in Ca3Co4Oy ceramics by Nd doping

AutorConstantinescu, G.; Torres, M. A.; Rasekh, Sh.; Madre, M. A.; Diez, J. C.; Sotelo, A.
Fecha de publicación2014
CitaciónJournal of Materials Science - Materials in Electronics 25(2): 922-927 (2014)
ResumenCa3-xNdxCo4Oy polycrystalline thermoelectric ceramics with small amounts of Nd have been synthesized by the classical solid state method. X-ray diffraction data have shown that all the Nd has been incorporated into the Ca3Co4O9 and Ca3Co2O6 phases and no Nd-containing secondary phases have been produced. Apparent density measurements have revealed that all samples are very similar, with densities around 70 % of the theoretical one. Electrical resistivity decreases in all Nd-doped samples, compared with the pure one, while Seebeck coefficient remains constant for all samples. The improvement in resistivity leads to higher power factor values than the obtained for the undoped samples. © 2013 Springer Science+Business Media New York.
Versión del editorhttp://dx.doi.org/10.1007/s10854-013-1665-5
Identificadoresdoi: 10.1007/s10854-013-1665-5
issn: 0957-4522
e-issn: 1573-482X
Aparece en las colecciones: (ICMA) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
Nd doping.pdf579,68 kBAdobe PDFVista previa
Mostrar el registro completo

NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.