Título

Mid IR emission from highly transparent Er3+ doped tellurite glass ce- ramic for bio applications

Autor Morea, Roberta ; Fernández, T. T.; Miguel, A.; Hernández, M.; Ulloa, J. M.; Fernández, Joaquín ; Balda, Rolindes ; Solís Céspedes, Javier ; Gonzalo de los Reyes, José
Fecha de publicación 10-jun-2014
EditorOptical Society of America
Citación CLEO 2014
ResumenIntense emission peaking at 2.18 ¿m was successfully obtained from erbium upon rigorous engineering of its glass host. Highly localized crystallization of erbium sites is substantiated by micro Raman and micro-PL along with TEM.
Descripción Conference on Lasers and Electro-Optics: Laser Science to Photonic Applications, San Jose, California, USA, 08 - 13 Jun 2014
URI http://hdl.handle.net/10261/114815
Aparece en las colecciones: (CFM) Comunicaciones congresos
(CFMAC-IEM) Comunicaciones congresos
(CFMAC-IO) Comunicaciones congresos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
RMorea.pdf976,51 kBUnknownVisualizar/Abrir
Mostrar el registro completo
 


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.