Nanoprecipitation of oxide particles and related high strength in oxide-dispersion-strengthened iron-aluminium-chromium intermetallics

Autor Morris, David G.; Muñoz-Morris, Mª Antonia
Palabras clave ODS materials
Mechanical properties
High-temperature deformation
Iron aluminides
Intermetallic phases
Fecha de publicación 2013
EditorElsevier
Citación Acta Materialia 61 (12): 4636-4647 (2013)
ResumenA series of oxide-dispersion-hardened Fe-Al-Cr iron aluminides has been prepared by mechanical alloying techniques producing compositions intermediate between binary Fe-Al and commercial Fe-Cr alloys. The very fine oxide particles form by precipitation on the {1 0 0} planes in the B2 ordered matrix, initially as a metastable face-centred cubic Y2O3 phase which later transforms to an Al-richer phase with monoclinic Al2Y 4O9 structure. The importance of this precipitation sequence in determining particle size and density is discussed. Mechanical properties are examined up to high temperatures, and strength is shown to depend mostly on the contribution of the fine particles, with also contributions from the fine grain size, and from the ordered matrix. The roles of elastic modulus variations, strongly affected by alloy composition, and of matrix strength variations in determining material strength are emphasized. Analysis of the factors determining particle nucleation rate and high-temperature strength leads to the development of predictive rules for improving microstructural refinement and strength. © 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
URI http://hdl.handle.net/10261/113653
DOI10.1016/j.actamat.2013.04.034
Identificadoresdoi: 10.1016/j.actamat.2013.04.034
issn: 1359-6454
Aparece en las colecciones: (CENIM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
accesoRestringido.pdf15,38 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 



NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.