Título: | ZrTiO4 materials obtained by spark plasma reaction-sintering |
Autor: | Borrell, Amparo; Salvador, M. D.; Rocha, Victoria G. CSIC ORCID ; Fernández, Adolfo CSIC ORCID; Gómez, Andrés; López-López, E. CSIC; Moreno, Rodrigo CSIC ORCID | Palabras clave: | Microstructure Mechanical properties Ceramic-matrix composites Sintering |
Fecha de publicación: | 2014 | Editor: | Elsevier | Citación: | Composites Part B: Engineering 56: 330-335 (2014) | Resumen: | Zirconium titanate (ZrTiO4), have many attractive properties such as high resistivity, high dielectric constant, high permittivity at microwave frequencies and excellent temperature stability for microwave properties. Zirconium titanate dense materials are proposed for many structural applications, but fully reacted and completely dense pieces are difficult to obtain by conventional routes. In this work, fully dense zirconium titanate materials (∼98%) were obtained at lower temperatures (1300-1400 C) and short processing time by non-conventional technique; spark plasma-reaction sintering (SPRS). Homogeneous and stable starting powders mixture with the adequate composition was prepared from the raw materials: m-ZrO2 (∼0.3 μm) and anatase-TiO2 (∼40 nm). Dense materials were mechanically and microstructural characterised. The fracture strength was measured by biaxial testing, giving values of about 200 MPa. © 2013 Published by Elsevier Ltd. All rights reserved. | URI: | http://hdl.handle.net/10261/113089 | DOI: | 10.1016/j.compositesb.2013.08.046 | Identificadores: | doi: 10.1016/j.compositesb.2013.08.046 issn: 1359-8368 |
Aparece en las colecciones: | (CINN) Artículos (ICV) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
accesoRestringido.pdf | 15,38 kB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
9
checked on 12-abr-2024
WEB OF SCIENCETM
Citations
10
checked on 26-feb-2024
Page view(s)
304
checked on 19-abr-2024
Download(s)
82
checked on 19-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.