Corrosion of magnesium-aluminum alloys with Al-11Si/SiC thermal spray composite coatings in chloride solution

Autor Arrabal, R.; Pardo, A.; Merino, M. C.; Mohedano, M.; Casajús, P.; Matykina, E.
Palabras clave Thermal spraying
Magnesium alloys
Composite coatings
Aluminum
Fecha de publicación 2011
EditorSpringer
Citación Journal of Thermal Spray Technology 20 (3): 569-579 (2011)
ResumenDepositions of Al-11Si coatings reinforced with 5, 15, and 30 vol.% SiC particles (SiCp) were performed onto AZ31, AZ80, and AZ91D magnesium alloys. The influence of substrate composition and SiCp proportion on the anti-corrosion properties of composite coatings was evaluated using DC and AC electrochemical measurements in 3.5 wt.% NaCl solution at 22 °C. The as-sprayed coatings were permeable to the saline solution, and galvanic corrosion occurred at the substrate/coating interface after immersion in the saline solution for a few hours. The addition of SiCp yielded coatings with higher porosity and less effectiveness against corrosion. The application of a cold-pressing post-treatment produced denser coatings with reduced surface roughness, improved hardness, and superior corrosion resistance. However, galvanic corrosion was observed after several days of immersion because of penetration of the 3.5 wt.% NaCl solution through the remaining pores in the coatings. © 2010 ASM International.
URI http://hdl.handle.net/10261/111628
DOI10.1007/s11666-010-9574-0
Identificadoresdoi: 10.1007/s11666-010-9574-0
issn: 1059-9630
Aparece en las colecciones: (CENIM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
accesoRestringido.pdf15,38 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 



NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.