Corrosion Behavior of AZ Magnesium Alloys with Al and Al-11 Si Thermal Spray Coatings

AutorPardo, A.; Merino, M. C.; Arrabal, R.; Casajús, P.; Mohedano, M.; Feliú Jr., S.; Merino, S.
Palabras claveAluminum coatings
Corrosion
Chloride
Aqueous environments
Thermal spraying
Fecha de publicación2011
EditorNACE International
CitaciónCorrosion 67 (2): 025003-1-025003-14 (2011)
ResumenThe corrosion behavior of AZ31, AZ80, and AZ91D Mg-Al-Zn alloys coated with aluminum and Al-11Si thermal spray was evaluated in 3.5 wt% sodium chloride (NaCl) solution at 22°C by gravimetric and electrochemical impedance spectroscopy (EIS) measurements. The corrosion products were examined using scanning electron microscopy (SEM), energy-dispersive x-ray analysis (EDX), and low-angle x-ray diffraction (XRD). The as-sprayed aluminum and Al-11Si coatings were porous, and galvanic corrosion of magnesium substrates was observed at the substrate/coating interfaces. Application of a cold-pressing posttreatment smoothed and densified the coatings, improved the contact between coating and substrate, and substantially increased the corrosion resistance. Cold-pressed aluminum coatings were an effective barrier against corrosion and revealed the same corrosion performance, regardless of the composition of the magnesium substrate. However, cold-pressed Al-11Si coatings were permeable to the chloride-containing solution, and galvanic corrosion of magnesium substrates was observed after a few days of immersion in 3.5 wt% NaCl solution.
URIhttp://hdl.handle.net/10261/111621
DOI10.5006/1.3549565
Identificadoresdoi: 10.5006/1.3549565
issn: 0010-9312
Aparece en las colecciones: (CENIM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
accesoRestringido.pdf15,38 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 

Artículos relacionados:


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.