Título

Fabrication of wire mesh-supported ZnO photocatalysts protected against photocorrosion

AutorVu, Thi Tan CSIC ORCID; Río, Laura del CSIC; Valdés-Solís Iglesias, Teresa CSIC ORCID ; Marbán Calzón, Gregorio CSIC ORCID
Palabras claveMethylene blue
Photocatalysis
Photocorrosion
ZnO
Stainless steel wire mesh
Fecha de publicaciónabr-2013
EditorElsevier
CitaciónApplied Catalysis B - Environmental 140-141: 189-198 (2013)
ResumenIn this work a catalyst consisting of high surface area ZnO nanoflowers supported on a stainless steel wire mesh was synthesized by hydrothermal growth, and tested for the catalytic photodegradation of methylene blue under UV irradiation. The stability of the photocatalyst was evaluated by assessing the evolution over several reaction stages of catalytic activity and ZnO loss. The initial high activity of this catalyst was followed by a significant decrease after successive reaction cycles due to the dissolution of the ZnO as a consequence of photocorrosion. Impregnation of the catalyst with small amounts of silver enhanced its initial catalytic activity, but failed to produce the photostabilisation of the catalyst that has been reported in the literature. Dip-coating the photocatalyst (either undoped or silver doped) with a diluted polysiloxane solution produced a transparent polysiloxane coating that completely prevented photocorrosion and allowed a stable catalytic activity to be maintained over 8 reaction stages at values higher than those obtained with uncoated catalysts after just 2–3 reactions stages with negligible loss of ZnO.
Versión del editorhttp://dx.doi.org/10.1016/j.apcatb.2013.04.023
URIhttp://hdl.handle.net/10261/111010
DOI10.1016/j.apcatb.2013.04.023
ISSN0926-3373
Aparece en las colecciones: (INCAR) Artículos




Ficheros en este ítem:
Fichero Descripción Tamaño Formato
Fabrication_wire_Vu.pdf1,94 MBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo

CORE Recommender

SCOPUSTM   
Citations

47
checked on 12-mar-2024

WEB OF SCIENCETM
Citations

44
checked on 29-feb-2024

Page view(s)

357
checked on 19-mar-2024

Download(s)

430
checked on 19-mar-2024

Google ScholarTM

Check

Altmetric

Altmetric


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.