Título

Synthesis and processing of spinel powders for transparent ceramics

AutorSuárez, Marta ; Rocha, Victoria G. ; Fernández, Adolfo ; Menéndez, José Luis ; Torrecillas, Ramón
Palabras claveSpinels
Optical properties
Sintering
Fecha de publicación2014
EditorElsevier
CitaciónCeramics International 40(3): 4065-4069 (2014)
ResumenSpinel powders have been synthesized by chemical coprecipitation using two different precursors, nitrates and chlorides, and by an oxides mixture route. It has been shown that depending on the precursors used and the synthesis conditions pure spinel nanopowder can be obtained at different temperatures and with different levels of agglomeration. According to TEM results, the chloride route allows obtaining pure and deagglomerated spinel powders after calcination at 800 C with a submicrometer particle size. Sintered lyophilized powders obtained by a chloride route allow achieving materials with in-line transmittances close to 46% at 540 nm and 83% in the infrared range. © 2013 Elsevier Ltd and Techna Group S.r.l.
Versión del editorhttp://dx.doi.org/10.1016/j.ceramint.2013.08.060
URIhttp://hdl.handle.net/10261/110916
DOI10.1016/j.ceramint.2013.08.060
Identificadoresdoi: 10.1016/j.ceramint.2013.08.060
issn: 0272-8842
Aparece en las colecciones: (CINN) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
accesoRestringido.pdf15,38 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 

Artículos relacionados:


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.