Título

LaNi0.6Co0 4O3-δ dip-coated on Fe-Cr mesh as a composite cathode contact material on intermediate solid oxide fuel cells

Autor Morán-Ruiz, Aroa; Vidal, Karmele; Larrañaga, Aitor; Laguna-Bercero, M. A.; Porras-Vázquez, Jose Manuel; Slater, P. R.; Arriortua, María Isabel
Palabras clave Ohmic resistance losses
Channeled interconnect
Composite contact material
IT-SOFC
Electrical contact
Fecha de publicación 2014
EditorElsevier
Citación Journal of Power Sources 269: 509-519 (2014)
ResumenThe feasibility of using Crofer22APU mesh dip coated with LaNi 0.6Co0.4O3-δ (LNC) ceramic paste as a uniform contact layer on a Crofer22APU channeled interconnect was studied. The control of LNC dip coating thickness on Fe-Cr mesh was carried out by rheological measurements of the suspension. SEM cross-section of formed composite contact material showed good adherence between ceramic and metallic components. The measured area specific resistance (ASR) value at 800 °C was 0.46 ± 0.01 mΩ cm2, indicating low contact resistance itself. The long term stability of metallic/ceramic composite was also studied. The contact resistance, when composite contact material was adhered to channeled Crofer22APU interconnect, was 5.40 ± 0.01 mΩ cm2, which is a suitable value for the performance of IT-SOFC stack. The stability of the system after treating at 800 °C for 1000 h was characterized using X-ray Micro-Diffraction (XRMD), Scanning Electron Microscope equipped with an Energy Dispersive X-ray analyzer (SEM-EDX) and X-ray Photoelectron Spectroscopy (XPS) techniques. The oxidation rate of the alloy and Fe3O4 phase formation were enhanced on the channels of the interconnect. Thus, the formation of CrO3 (g) and CrO2(OH)2 (g) species was accelerated on the composite surface under the channel. Through XRMD and XPS analysis the coexistence of two perovskite phases (initial LNC and Cr-perovskite) was observed. © 2014 Elsevier Ltd. All rights reserved.
Versión del editorhttp://dx.doi.org/10.1016/j.jpowsour.2014.07.040
URI http://hdl.handle.net/10261/102966
DOI10.1016/j.jpowsour.2014.07.040
Identificadoresdoi: 10.1016/j.jpowsour.2014.07.040
issn: 0378-7753
Aparece en las colecciones: (ICMA) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
MoranetalJPS14.pdf6,77 MBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 



NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.