Fabrication and characterization of graded anodes for anode-supported solid oxide fuel cells by tape casting and lamination

Autor Beltran, J.; Laguna-Bercero, M. A.; Gurauskis, J.; Peña, J. I.
Palabras clave Ni-YSZ
SOFC
Anode-supported
Lamination
Tape casting
Fecha de publicación 2014
EditorSpringer
Citación Electrocatalysis 5(3): 273-278 (2014)
ResumenGraded anodes for anode-supported solid oxide fuel cells (SOFCs) are fabricated by tape casting and subsequent cold lamination of plates using different compositions. Rheological parameters are adjusted to obtain stable suspensions for tape casting. The conditions for the tape casting and lamination will be described. Flexural strength of the reduced cermets measured using three-point bending configuration is 468 ± 37 MPa. The graded anode supports are characterized by scanning electron microscope observations, mercury porosimetry intrusion, and resistivity measurements, showing an adequate and homogeneous distribution of nickel, zirconia, and pores. The laminated samples showed a total porosity of 18.7 % (in vol%) and a bimodal pore size distribution centered in 20 and 150 nm, and the measured electrical resistivity of this sample was 120 ± 12 μΩ cm. The novelty of the present work is the lamination of tapes at room temperature without using plasticizers. This is made by the combination of two different binders with varying Tg (glass transition temperature) which resulted in plastic deformation at room temperature. Those results indicate that the proposed process is a cost-effective method to fabricate anode-supported SOFCs. © 2014 Springer Science+Business Media New York.
Versión del editorhttp://dx.doi.org/10.1007/s12678-014-0193-2
URI http://hdl.handle.net/10261/102963
DOI10.1007/s12678-014-0193-2
Identificadoresdoi: 10.1007/s12678-014-0193-2
e-issn: 1868-5994
issn: 1868-2529
Aparece en las colecciones: (ICMA) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
graded anodes.pdf463 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 



NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.