Leaching of borate waste cement matrices: Pore solution and solid phase characterization
Hernández, M. S.
Guerrero Bustos, Ana María
Goñi Elizalde, Sara
Cement
The chemical composition of the pore solution expressed from matrices of simulated borate liquid waste (containing H3BO3, Na2SO4, Na2HPO4 and Ca3(PO4)2) and pozzolanic cement (Spanish type IV-35) and the changes caused by leaching over 180 days in deionized water at temperatures of 20 and 40 °C were studied. The leaching was carried out according to the ANSI/ANS-16.1-1986 test. In addition, the change of the solid phase was characterized by X-ray diffraction, infrared spectroscopy and scanning electron microscopy.
2020-07-01T13:40:09Z
2020-07-01T13:40:09Z
2000-01
2020-07-01T13:40:11Z
artículo
http://purl.org/coar/resource_type/c_6501
doi: 10.1680/adcr.2000.12.1.1
issn: 0951-7197
e-issn: 1751-7605
Advances in Cement Research 12(1): 1-8 (2000)
http://hdl.handle.net/10261/215801
10.1680/adcr.2000.12.1.1
http://dx.doi.org/null
Sí
none
Thomas Telford