High-sensitivity radioluminescence (RL) and thermoluminescence (TL) measurements were carried out on samples of natural leucite (with 2.95% of Na2O) from Campania Vessa (Italy). Samples were annealed to modify the charge compensation through alkali metal self-diffusion and to produce luminescence centres. High-temperature powder diffraction, scanning electron microscopy and chemical analyses were performed to monitor the tetragonal–cubic phase transitions and the thermal drainage of alkali metal ions from the aluminosilicate lattice. The emission spectral bands of leucite (300, 380, 430, 480, 560 and 680 nm) match those of other Na/K-aluminosilicates (alkali metal feldspars) and could be attributed to similar defects. TL glow curves of increasingly pre-irradiated natural leucite (range 0–20 Gy) showed no changes above 300 °C, whereas some changes were observed with annealed samples (1000 °C for 12 h). This temperature is the starting point of Na self-diffusion within the aluminosilicate lattices. The areas of the TL glow curves of both natural and annealed ß-irradiated leucites can be fitted with a linear function with high correlation. These results are in agreement with high alkali metal loss (K2O 12% and Na2O 18%) during thermal pre-treatment, high cell volume expansion (from 2350 to 2500 Å) and the cubic Ia3d↔tetragonal I41/a phase transition. This promotes the egress of alkali metal ions and the production of [AlO4/M+]°, [AlO4/H+]° and [AlO4]° luminescence centres.
eng
openAccess
radioluminescence
thermoluminescence
leucite
Campania Vessa
Italy
Analysis of luminescence spectra of leucite (KAlSiO4)
artículo
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
URL
https://digital.csic.es/bitstream/10261/3218/2/Analyst%2c%202001%2c%20126%2c%20911-916.pdf
File
MD5
3c25bbe1edc64393640f4a5991fa9da5
334326
application/pdf
Analyst, 2001, 126, 911-916.pdf
URL
https://digital.csic.es/bitstream/10261/3218/3/Analyst%20Articles.mht
File
MD5
86355f6c6179ef55cf09694c41b79af0
113578
application/octet-stream
Analyst Articles.mht
URL
https://digital.csic.es/bitstream/10261/3218/6/Analyst%2c%202001%2c%20126%2c%20911-916.pdf.txt
File
MD5
77fe70bd1f7d1a5a04e8b4d898adc766
29690
text/plain
Analyst, 2001, 126, 911-916.pdf.txt