Título: | Ordered arrays of ferromagnetic, compositionally graded Cu 1-xNix alloy nanopillars prepared by template-assisted electrodeposition |
Autor: | Varea, Aïda; Suriñach, Santiago; Baró, María Dolors; Nogués, Josep CSIC ORCID; Sort, Jordi CSIC ORCID; Pellicer, Eva CSIC ORCID | Fecha de publicación: | 2013 | Editor: | Royal Society of Chemistry (UK) | Citación: | Journal of Materials Chemistry C 1(43): 7215-7221 (2013) | Resumen: | Periodic arrays of compositionally graded Cu-Ni alloy nanopillars (100 or 200 nm in diameter and 450 nm in height) have been fabricated by means of potentiostatic electrodeposition into patterned Au/Ti/Si(111) substrates using a single electrolytic solution. The pillars do not bend after the template removal but remain straight and perfectly attached to the substrate. The average composition of the alloy nanopillars can be tuned between 34 and 70 at% of Ni by varying the applied potential from a [Ni(ii)]/[Cu(ii)] = 95.2 electrolytic solution. The nanopillars are Ni-rich at the bottom with a compositional gradient about ±20-25% above/below the average composition. The magnetic characterization reveals that all the nanopillars are ferromagnetic with coercivity values around 100-150 Oe (in-plane) and 200-500 Oe (out-of-plane), which are larger than those for continuous films of similar average composition. Atom probe tomography of the Cu-rich Cu-Ni nanopillars indicates the segregation of Ni, which would explain their unexpected magnetic character. The graded-anisotropy ferromagnetic Cu-Ni pillars could be potentially applied in several fields including micro/nano-electromechanical systems (MEMS/NEMS), magnetic recording media or spintronics. © The Royal Society of Chemistry 2013. | URI: | http://hdl.handle.net/10261/99505 | DOI: | 10.1039/C3TC31310G | Identificadores: | doi: 10.1039/C3TC31310G issn: 2050-7534 |
Aparece en las colecciones: | (CIN2) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
accesoRestringido.pdf | 15,38 kB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
WEB OF SCIENCETM
Citations
10
checked on 22-feb-2024
Page view(s)
320
checked on 16-abr-2024
Download(s)
85
checked on 16-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.