Título: | Cyclic fatigue life- and crack-growth behavior of zirconia-niobium composites |
Autor: | Smirnov, Anton CSIC ORCID; Gutiérrez-González, C. F. CSIC ORCID; Bartolomé, Jose F. CSIC ORCID | Fecha de publicación: | 2013 | Editor: | Wiley-Blackwell | Citación: | Journal of the American Ceramic Society 96(6): 1709-1712 (2013) | Resumen: | A 3Y-TZP/Nb composite fabricated by Hot-pressing (HP) sintering with well-distributed lamellar/flake-shaped metal particles (20 vol% fraction) has been studied under cyclic loading. Fatigue life was determined for the ceramic/metal composite as well as for monolithic zirconia to compare the sensitivities of both materials to cyclic stresses. In both cases, the fatigue test was performed according to ISO 6872. It was found that the 3Y-TZP/Nb composite exhibits fatigue behavior which was compared with monolithic zirconia. The growth of fatigue cracks influences the bridging actions of the metallic grains and causes significant degradation in the mechanical properties of the composite material. © 2013 The American Ceramic Society. | URI: | http://hdl.handle.net/10261/82926 | DOI: | 10.1111/jace.12384 | Identificadores: | doi: 10.1111/jace.12384 issn: 0002-7820 e-issn: 1551-2916 |
Aparece en las colecciones: | (ICMM) Artículos (CINN) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
accesoRestringido.pdf | 15,38 kB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
13
checked on 27-mar-2024
WEB OF SCIENCETM
Citations
12
checked on 22-feb-2024
Page view(s)
269
checked on 28-mar-2024
Download(s)
83
checked on 28-mar-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.