Título: | Corrosion inhibition of aluminum by coatings formulated with Al-Zn-vanadate hydrotalcite |
Autor: | Vega, J. M. CSIC; Granizo, N. CSIC; Fuente, Daniel de la CSIC ORCID; Simancas Peco, Joaquín CSIC; Morcillo, Manuel CSIC ORCID | Fecha de publicación: | 2011 | Editor: | Elsevier | Citación: | Progress in Organic Coatings 70: 213- 219 (2011) | Resumen: | The hydrotalcite structure is an ionic lamellar solid with positively charged layers incorporating two kinds of metallic cations and hydrated gallery anions. The ability of these compounds to retain aggressive ions and simultaneously release a corrosion inhibitor is the main reason for the development of hydrotalcite compounds to replace hexavalent chromium compounds (chromates) as inhibitive pigments. In this study, alkyd coatings formulated with Al-Zn-vanadate hydrotalcite, at different pigment concentrations were applied on aluminum specimens. The painted panels were subjected to different accelerated tests (condensing humidity, salt spray and Kesternich) and atmospheric exposure in atmospheres of different aggressiveness. Corrosion performance was evaluated by electrochemical impedance spectroscopy (EIS). A traditional zinc chromate pigment was also tested for comparative purposes. The obtained results confirm that hydrotalcite compounds achieve corrosion inhibition of the underlying aluminum substrate. It has been shown that an increase of anticorrosive pigment content (for a constant pigment volume concentration) does not always improve the primer behavior, but a larger amount of vanadates released from Al-Zn-vanadate hydrotalcite particles does improve anticorrosive behavior. © 2010 Elsevier B.V. All rights reserved. | URI: | http://hdl.handle.net/10261/75591 | DOI: | 10.1016/j.porgcoat.2010.08.014 | Identificadores: | doi: 10.1016/j.porgcoat.2010.08.014 issn: 0300-9440 |
Aparece en las colecciones: | (CENIM) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
Corrosion inhibition.pdf | 509,72 kB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
61
checked on 22-abr-2024
WEB OF SCIENCETM
Citations
56
checked on 28-feb-2024
Page view(s)
332
checked on 23-abr-2024
Download(s)
737
checked on 23-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.