Título : Microstructural Characterization of AI-Rich Ni-Cr-AI Cast Alloys
Autor : González-Carrasco, José Luis; Adeva, Paloma; Cristina del Peso, Carmen; Aballe, Miguel
Fecha de publicación : 1994
Editor: Elsevier
Citación : Materials Characterization 32 (2) : 135-145 (1994)
Resumen: Several Ni-Cr-A1 alloys, with up to 30 at.% A1, were prepared in an induction furnace and cast under inert atmosphere. All alloys were homogenized for 8 h at 1473K under an argon atmosphere, followed by treatments at temperatures between 1023 and 1273K for times up to 180 h. These alloys contain phases that are to a great extent, structurally similar. This is frequently complicated further by their particle size and their degree of order. Their characterization is not always simple and usually must be based on more than one technique. In this work the microstructural evolution was studied by means of light microscopy, scanning electron microscopy and microanalysis, and x-ray diffraction techniques. For completeness, hardness and microhardness tests were performed to evaluate the precipitation phenomenon
Versión del editor: http://dx.doi.org/10.1016/1044-5803(94)90076-0
URI : http://hdl.handle.net/10261/57902
ISSN: 1044-5803
DOI: 10.1016/1044-5803(94)90076-0
Aparece en las colecciones: (CENIM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
Embargo_Gral.pdf21,67 kBAdobe PDFVisualizar/Abrir
Mostrar el registro completo
Enlaces SFX CSICSFX Query

NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.