Closed Access item Nanoscale austenite reversion through partitioning, segregation and kinetic freezing: Example of a ductile 2 GPa Fe–Cr–C steel

Authors:Yuan, L.
Ponge, D.
Wittig, J.
Choi, P.
Jiménez, José Antonio
Raabe, D.
Keywords:Austenite reversion, Partitioning, Diffusion, Strength, Ductility
Issue Date:2012
Publisher:Elsevier
Citation:Acta Materialia 60(6-7) : 2790-2804 (2012)
Abstract:Austenite reversion during tempering of a Fe–13.6 Cr–0.44 C (wt.%) martensite results in an ultra-high-strength ferritic stainless steel with excellent ductility. The austenite reversion mechanism is coupled to the kinetic freezing of carbon during low-temperature partitioning at the interfaces between martensite and retained austenite and to carbon segregation at martensite–martensite grain boundaries. An advantage of austenite reversion is its scalability, i.e. changing tempering time and temperature tailors the desired strength–ductility profiles (e.g. tempering at 400 °C for 1 min produces a 2 GPa ultimate tensile strength (UTS) and 14% elongation while 30 min at 400 °C results in a UTS of ∼1.75 GPa with an elongation of 23%). The austenite reversion process, carbide precipitation and carbon segregation have been characterized by X-ray diffraction, electron back-scatter diffraction, transmission electron microscopy and atom probe tomography in order to develop the structure–property relationships that control the material’s strength and ductility.
Publisher version (URL):http://dx.doi.org/10.1016/j.actamat.2012.01.045
URI:http://hdl.handle.net/10261/57295
ISSN:1359-6454
???metadata.dc.identifier.doi???:10.1016/j.actamat.2012.01.045
Appears in Collections:(CENIM) Artículos

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.