Título: | Analysis of the microstructure evolution during tensile testing at room temperature of high-manganese austenitic steel |
Autor: | Jiménez, José Antonio CSIC ORCID ; Frommeyer, G. | Palabras clave: | TWIP steel Tensile test Microstructure Texture |
Fecha de publicación: | 2010 | Editor: | Elsevier | Citación: | Materials Characterization 61(2) : 221-226 (2010) | Resumen: | The microstructure and texture evolution of low-stacking fault energy high-manganese austenitic steel during tensile testing at room temperature was studied by means of interrupted tests. Untested material shows fully recrystallized austenitic grains and an almost random texture. During deformation, two deformation mechanisms, mechanical twinning and dislocation gliding, compete with each other. The governing mechanism of a single grain will depend on its crystallographic orientation relative to tensile direction. As a result of the strong interaction between grain orientation and twinning activity at low tensile strain, both grains with and without deformation twins can be observed. However, at high strain all the grains exhibited twin bands. Tensile tested samples were characterized by the presence of a fiber texture with the <111> and <100> directions parallel to the tensile direction. | Versión del editor: | http://dx.doi.org/10.1016/j.matchar.2009.11.013 | URI: | http://hdl.handle.net/10261/57258 | DOI: | 10.1016/j.matchar.2009.11.013 | ISSN: | 1044-5803 |
Aparece en las colecciones: | (CENIM) Artículos |
Mostrar el registro completo
CORE Recommender
SCOPUSTM
Citations
91
checked on 09-abr-2024
WEB OF SCIENCETM
Citations
82
checked on 28-feb-2024
Page view(s)
377
checked on 19-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.