Título: | Defect analysis of Fe3(Al1– x Si x ) alloys by positron-lifetime spectroscopy |
Autor: | Ortega, Y.; Diego, N. de; Jiménez, José Antonio CSIC ORCID ; Río del, J. | Palabras clave: | Transition element alloys Aluminium alloys Iron base alloys Silicon |
Fecha de publicación: | 2004 | Editor: | Taylor & Francis | Citación: | Philosophical Magazine Letters 84(9) : 547-554 (2004) | Resumen: | The recovery behaviour of vacancy-type defects created at 1000°C in Fe3(Al1-xSix) alloys has been investigated by positron-lifetime measurements in samples cooled to room temperature by water quenching, air quenching and furnace cooling. In addition, a set of samples was aged for one week at 520°C. After water quenching, measurements reveal a high concentration of thermal vacancies, and from the decrease of the average positron lifetime it is inferred that vacancy recovery is strongly composition-dependent. Greater decreases of the positron lifetime were found for Si-rich samples, suggesting diffusion enhancement as the Si concentration increases. For the Fe3Al alloy, the retained vacancy concentration depends strongly on the cooling rate. This is related to atomic ordering and a rebuilding of the D03 structure. | Versión del editor: | http://dx.doi.org/10.1080/09500830412331313338 | URI: | http://hdl.handle.net/10261/57086 | DOI: | 10.1080/09500830412331313338 | ISSN: | 0950-0839 |
Aparece en las colecciones: | (CENIM) Artículos |
Mostrar el registro completo
CORE Recommender
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.