Title: Oxidation behaviour of aTi–46Al–1Mo–0.2Si alloy: the effect of Mo addition and alloy microstructure
Authors: Pérez, P., Jiménez, José Antonio, Frommeyer, G., Adeva, Paloma
Keywords: γ-TiAl based intermetallic alloy
High temperature oxidation
Microstructure
Alloying
Issue Date: 2000
Publisher: Elsevier
Abstract: The influence of molybdenum addition and alloymicrostructure on the oxidationbehaviour of aTi–46.8Al–1Mo–0.2Si alloy was studied in air at temperatures ranging from 600 to 900°C. The alloy produced by arc melting exhibited a structure of coarse lamellar grains in as-cast condition that transformed to a duplex microstructure after hot extrusion at 1300°C. Oxidation rate and scale spallation resistance were not affected by the type of microstructure. The effect of molybdenum addition was related to the formation and thickening of a protective continuous nitride layer. The low mass gain measured can be associated with the low oxidation rate of the nitride layer. Finally, the poor spalling resistance of the oxide scale at 900°C was attributed to the mismatch in thermal expansion coefficients of the oxide scale and the nitride layer.
Publisher version (URL): http://dx.doi.org/10.1016/S0921-5093(00)00755-3
URI: http://hdl.handle.net/10261/56617
ISSN: 0921-5093
???metadata.dc.identifier.doi???: 10.1016/S0921-5093(00)00755-3
Citation: Materials Science and Engineering - A 284(1-2) : 138-147 (2000)
Appears in Collections:(CENIM) Artículos

Files in This Item:
There are no files associated with this item.
Show full item record
 
CSIC SFX LinksSFX Query


Items in Digital.CSIC are protected by copyright, with all rights reserved, unless otherwise indicated.