|Autor :||Segovia, M.|
Sotomayor Torres, C. M.
|Fecha de publicación :||2012|
|Editor:||Taylor & Francis|
|Citación :||Molecular Crystals and Liquid Crystals 555(1): 40-50 (2012)|
|Resumen:||The synthesis, characterization, and properties of three types of one-dimensional zinc oxide nanostructures are described. They were obtained by solvothermal treatment of nanometric zinc oxide as zinc ion source (i.e., starting from pure oxide), from a mixture of the oxide with stearic acid, and from intercalated oxide in the layered nanocomposite ZnO(stearic acid)0.38. The reactions were performed at 180C in a (1:1) ethanol/water mixture. Depending on the precursor and reaction times, morphologically homogenous phases corresponding to ZnO nanoneedles, nanorods or nanowires were obtained. Photoluminescence emissions were observed and are attributed to exciton transitions and to the presence of intrinsic defects such as oxygen and zinc interstitials. The band gap energies (Eg) were comparable to the values of bulk ZnO. The prepared nanostructures showed photocatalytic activities with respect to the degradation of methylene blue which were comparable to that of bulk zinc oxide. © 2012 Copyright Taylor and Francis Group, LLC.|
|Aparece en las colecciones: ||(CIN2) Artículos|
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.