Título

Influence of strain rate on recrystallisation– precipitation interaction in V, Nb, and V–Ti microalloyed steels

AutorMedina, Sebastián F. CSIC ORCID; Quispe, Alberto
Palabras claveRecrystallisation-precipitation
Microalloyed steels
RPTT diagrams
Fecha de publicación2000
EditorW.S. Maney & Son
CitaciónMaterials Science and Technology 16 (6) : 635-642 (2000)
ResumenA study has been made of the recrystallisation?precipitation interaction in three microalloyed steels, containing respectively V, Nb, and V?Ti, applying two different strain rates. Recrystallised fraction v.time curves were determined and used to draw recrystallisation?precipitation?time?temperature (RPTT) diagrams. The influence of strain rate has been shown to be similar in the three steels. On the basis of the results the value of }}SB0?19 has been found for the exponent of the strain rate, following Dutta and Sellars'model for the parameter t0?05 , which differs from the value }}SB0?5 proposed by these authors. Simultaneously, the influence of strain rate on the static recrystallis ation critical temperature has been determined, it being observed that an increase in the former leads to a drop in the latter. Furthermore, strain rate is shown to have an influence on the recrystallisation?precipitation interaction, acting on those parameters that best contribute to defining RPTT diagrams In this sense, it was found that an increase in the strain rate led to a drop in the curve nose temperature TN and a reduction in the time necessary for precipitation to finalise t0?95 , as well as an increase in the recrystallisation rate.A study has been made of the recrystallisation?precipitation interaction in three microalloyed steels, containing respectively V, Nb, and V?Ti, applying two different strain rates. Recrystallised fraction v.time curves were determined and used to draw recrystallisation?precipitation?time?temperature (RPTT) diagrams. The influence of strain rate has been shown to be similar in the three steels. On the basis of the results the value of }}SB0?19 has been found for the exponent of the strain rate, following Dutta and Sellars'model for the parameter t0?05 , which differs from the value }}SB0?5 proposed by these authors. Simultaneously, the influence of strain rate on the static recrystallis ation critical temperature has been determined, it being observed that an increase in the former leads to a drop in the latter. Furthermore, strain rate is shown to have an influence on the recrystallisation?precipitation interaction, acting on those parameters that best contribute to defining RPTT diagrams In this sense, it was found that an increase in the strain rate led to a drop in the curve nose temperature TN and a reduction in the time necessary for precipitation to finalise t0?95 , as well as an increase in the recrystallisation rate.
Versión del editorhttp://dx.doi.org/10.1179/026708300101508405
URIhttp://hdl.handle.net/10261/47063
DOI10.1179/026708300101508405
ISSN0267-0836
Aparece en las colecciones: (CENIM) Artículos

Mostrar el registro completo

CORE Recommender

SCOPUSTM   
Citations

19
checked on 23-mar-2024

WEB OF SCIENCETM
Citations

15
checked on 16-feb-2024

Page view(s)

351
checked on 28-mar-2024

Google ScholarTM

Check

Altmetric

Altmetric


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.