Título: | Characteristics and thermal detinning of ferrous scrap from Spanish MSW compost plants |
Autor: | López-Delgado, Aurora CSIC ORCID ; Lobo Recio, María Angeles; Peña, Carmen; López, Víctor CSIC; López Gómez, Félix Antonio CSIC ORCID CVN | Palabras clave: | Ferrous scrap Compost plant Detinning MSW |
Fecha de publicación: | 2005 | Editor: | Elsevier | Citación: | Resources, Conservation and Recycling 44 (2) : 167-183 (2005) | Resumen: | Twenty samples of ferrous scrap from different Spanish municipal solid waste (MSW) compost plants were characterised in order to knowtheir composition and tin contents, with a viewto evaluating their metallurgical quality as a raw material for the steel industry. Eighty five percent of the samples had a high metallic fraction weight percentage, constituted principally by food and beverage cans and domestic aerosols. The average tin contentwas 0.43 wt.%. The ferrous scrap samples were subjected to fragmentation, cleaning and thermal detinning processes in order to improve their quality. The products obtained were chemically, mineralogically, metallographically and spectroscopically characterised. The thermal detinning process, performed at a relatively high temperature (700 ◦C) and with a short sample holding time in the furnace (10 min), yielded a very high quality ferrous scrap with a very low tin content (<0.05 wt.%) and a low oxidation degree of the steel. The corrosion degree in these conditions was practically negligible. | Versión del editor: | http://dx.doi.org/10.1016/j.resconrec.2004.11.003 | URI: | http://hdl.handle.net/10261/46014 | DOI: | 10.1016/j.resconrec.2004.11.003 | ISSN: | 0921-3449 |
Aparece en las colecciones: | (CENIM) Artículos |
Mostrar el registro completo
CORE Recommender
SCOPUSTM
Citations
2
checked on 18-abr-2024
WEB OF SCIENCETM
Citations
2
checked on 26-feb-2024
Page view(s)
362
checked on 24-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.