Título: | Vidrios de silicato a partir de residuos galvánicos con alto contenido en Cr y Ni |
Otros títulos: | Glass silicate from Cr and Ni high level galvanic waste | Autor: | Esteban-Cubillo, A. CSIC; Pecharromán, Carlos CSIC ORCID CVN ; Mello-Castanho, Sonia; Silva, A. C. da; Moya, J. S. CSIC | Palabras clave: | Lama galvánica Vídrio silicatos Procesos de inertizatión Galvanic waste Silicate glass and inertization process |
Fecha de publicación: | ene-2006 | Editor: | Sociedad Española de Cerámica y Vidrio | Citación: | Boletín de la Sociedad Española de Cerámica y Vidrio 45(1): 52-57 (2006) | Resumen: | [ES] La eliminación de los residuos industriales tóxicos, es en la actualidad un objetivo prioritario a nivel mundial. Para el
caso particular de los residuos sólidos galvánicos, su alto contenido en metales pesados resulta perjudicial tanto para la
salud como para el medio ambiente. En este trabajo se han obtenido vídrios con un 40% en peso de residuos galvánicos
de alto contenido en cromo y níquel. La estabilidad química de los vídrios obtenidos fue comprobada mediante ensayos
de resistencia al ataque hidrolítico, ácido y alcalino. Finalmente, los diferentes vídrios fueron caracterizados por diferentes
técnicas difración de rayos-X, fluorescencia de rayos-X, espectrometría infrarroja. [EN] The environmental and human health related with harmful industrial waste is nowadays an issue of worldwide great concern. Particularly the case of galvanic solid waste, because of its high content in heavy metals, it is highly harmful from both environmental and human health point of view. In this study, glasses containing up to 40 wt% of galvanic waste with a high content of chromium and nickel were obtained. The chemical stability of these glasses was studied by hydrolytic, alkaline and acid attack. Finally the different glasses were studied by X-ray diffraction, X-ray fluorescence and infrared spectroscopy techniques in order to rationalize and to understand its observed chemical stability. |
Versión del editor: | http://boletines.secv.es/es/index.php?id=4&vol=45 | URI: | http://hdl.handle.net/10261/4145 | ISSN: | 0366-3175 |
Aparece en las colecciones: | (ICMM) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
silicato.pdf | 590,17 kB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
Page view(s)
509
checked on 19-mar-2024
Download(s)
309
checked on 19-mar-2024
Google ScholarTM
Check
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.