| Título: | In situ reduction of (100) SrTiO3 |
Autor: | Martín-González, Marisol CSIC ORCID ; Aguirre, Myriam H. CSIC ORCID; Morán, Emilio; Alario-Franco, Miquel Á.; Pérez-Dieste, Virginia; Ávila, José CSIC ORCID; Asensio, María C. CSIC ORCID | Palabras clave: | Strontium titanate Reduction PES LEED Ordered oxygen vacancies |
Fecha de publicación: | 1-sep-2000 | Editor: | Elsevier | Citación: | Solid State Sciences 2 (2000) 519–524 | Resumen: | Low energy electron diffraction (LEED) and photoelectron spectroscopy (PES) have been employed to study the (100) SrTiO3 surface annealed in ultra high vacuum. The annealing was performed up to 830°C. After annealing at 830°C, we have observed from PES spectra the appearance of the conduction band and from LEED patterns the (√5 x √5)R 26.6° superstructure. Both features seem to have the same origin: the ordering of oxygen vacancies. | Versión del editor: | http://dx.doi.org/10.1016/S1293-2558(00)01068-2 | URI: | http://hdl.handle.net/10261/26271 | DOI: | 10.1016/S1293-2558(00)01068-2 | ISSN: | 1293-2558 |
| Aparece en las colecciones: | (IMN-CNM) Artículos (ICMM) Artículos |
Ficheros en este ítem:
| Fichero | Descripción | Tamaño | Formato | |
|---|---|---|---|---|
| Martín González, M.S. et al Solid State Sciences_2_2000.pdf | 1,65 MB | Adobe PDF |  Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
43
checked on 24-abr-2024
WEB OF SCIENCETM
Citations
42
checked on 22-feb-2024
Page view(s)
343
checked on 22-abr-2024
Download(s)
521
checked on 22-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.