Título: | Control of the Length of Fe73.5Si13.5Nb3Cu1B9 Microwires to Be Used for Magnetic and Microwave Absorbing Purposes |
Autor: | Gueye,Papa Gorgui Birame; López-Sánchez, Jesús CSIC ORCID; Navarro, Elena; Serrano Rubio, Aída CSIC ORCID ; Marín, Pilar CSIC ORCID | Palabras clave: | Microwave absorbing composites Tunable magnetic properties Multifunctional microwires Ball milling Filtering/sedimentation optimization processes FeSiNbCuB microwires |
Fecha de publicación: | 6-mar-2020 | Editor: | ACS Publications | Citación: | ACS Applied Electronic Materials 12: 15644- 15656 (2020) | Resumen: | A combination of high-energy ball milling, vacuum filtering, and sedimentation processes has been demonstrated to be a useful approach to reduce, in a controlled way, the length of as-cast Fe73.5Si13.5Nb3Cu1B9 amorphous magnetic microwires (MWs) and annealed material at 550 °C in nitrogen conditions. Homogeneous compositional microstructures with fairly narrow size distributions between 1300 and 11.7 μm are achieved, exhibiting tunable response as a soft magnetic material and as a microwave absorber. From the magnetic perspective, the soft magnetic character is increased with smaller length of the MWs, whereas the remanence has the opposite behavior mainly due to the structural defects and the loss of the shape anisotropy. From the microwave absorption perspective, a novel potential applicability is tested in these refined microstructures. This innovation consists of coatings based on commercial paints with a filling percentage of 0.55% of MWs with different lengths deposited on metallic sheets. Large attenuation values around −40 dB are obtained in narrow spectral windows located in the GHz range, and their position can be varied by combining different optimized lengths of MW. As an example of this powerful mechanism for absorbing microwaves at specific frequencies, MW lengths of 2 mm and 50 μm are chosen, where precise tailoring of the minimum reflection loss (RL) is obtained in a range between 8.85 and 13.25 GHz. To confirm these experimental results, an effective medium standard model proposed for electrical permittivity is used. Experimental and theoretical results are consistent and these novel composites are also proposed as a feasible candidate for designing frequency-selective microwave absorbers on demand, with low filling percentages and high absorption intensity values. | Versión del editor: | http://dx.doi.org/10.1021/acsami.9b21865 | URI: | http://hdl.handle.net/10261/232477 | DOI: | 10.1021/acsami.9b21865 | E-ISSN: | 2637-6113 |
Aparece en las colecciones: | (ICV) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
accesoRestringido.pdf | 15,38 kB | Adobe PDF | Visualizar/Abrir | |
Gueye_Control_ACS_Applied_Electronic_Materials _2020_postprint.pdf | 2,18 MB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
22
checked on 06-abr-2024
WEB OF SCIENCETM
Citations
19
checked on 27-feb-2024
Page view(s)
85
checked on 23-abr-2024
Download(s)
182
checked on 23-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.