| Título: | Mechanically stable monoclinic zirconia-nickel composite |
Autor: | Moya, J. S. CSIC; López-Esteban, Sonia CSIC ORCID; Pecharromán, Carlos CSIC ORCID CVN ; Bartolomé, Jose F. CSIC ORCID; Torrecillas, Ramón CSIC ORCID CVN | Fecha de publicación: | 2002 | Editor: | American Ceramic Society John Wiley & Sons |
Citación: | Journal of the American Ceramic Society 85(8): 2119-2121 (2002) | Resumen: | A dense (>98% theoretical density), residual‐stress‐free m‐ZrO2/40 vol% nickel composite with K IC∼ 5.4 MPa·m1/2 and ςf∼ 225 MPa has been obtained using a simple wet processing route and subsequent sintering at 1430°C in a 90% argon/10% hydrogen atmosphere. The mechanism for release of internal stresses by the composite developed during the t → m transformation on cooling is explained in terms of plastic flow in the infinite nickel cluster formed at the percolation threshold. | Versión del editor: | https://doi.org/10.1111/j.1151-2916.2002.tb00416.x | URI: | http://hdl.handle.net/10261/223436 | DOI: | 10.1111/j.1151-2916.2002.tb00416.x | Identificadores: | doi: 10.1111/j.1151-2916.2002.tb00416.x issn: 0002-7820 |
| Aparece en las colecciones: | (INCAR) Artículos (ICMM) Artículos |
Ficheros en este ítem:
| Fichero | Descripción | Tamaño | Formato | |
|---|---|---|---|---|
| accesoRestringido.pdf | 15,38 kB | Adobe PDF |  Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
15
checked on 10-abr-2024
WEB OF SCIENCETM
Citations
13
checked on 25-feb-2024
Page view(s)
93
checked on 23-abr-2024
Download(s)
40
checked on 23-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.