Título: | Efecto de la adición de un 10 % en volumen de cromo en el comportamiento a tracción de aleaciones pulvimetalúrgicas NiAlCr |
Otros títulos: | Effect of the addition of 10 % (volume fraction) of chromium on the mechanical properties of NiAICr processed by powder metallurgy | Autor: | García-Barriocanal, Javier; Garcés, Gerardo CSIC ORCID; Pérez Zubiaur, Pablo CSIC ORCID; Adeva, Paloma CSIC ORCID CVN | Palabras clave: | NI3AL Microestructura Propiedades mecánicas Pulvimetalurgia Microstructure Mechanical properties Powder metallurgy |
Fecha de publicación: | 30-ago-2005 | Editor: | Consejo Superior de Investigaciones Científicas (España) | Citación: | Revista de Metalurgia 41(4): 286-291 (2005) | Resumen: | [ES] En este trabajo se estudia la influencia de la adición de un 10 % en volumen, de cromo en
las propiedades mecánicas de aleaciones NI3Al-Cr procesadas por vía pulvimetalúrgica.
Para ello se prepararon dos aleaciones: la primera, se obtuvo por molienda de polvo de
composición Ni-20,9Al-8Cr-0,49B (% at.) y, a la segunda, se le añadió un 10 % en
volumen de partículas de cromo, mediante un proceso de mezcla, previo al de molienda.
Ambas, fueron consolidadas mediante compactación isostática en caliente (HIP) y, por
último, se les aplicaron tratamientos térmicos para homogeneizar la microestructura. Los
resultados experimentales han mostrado que el refuerzo de cromo tiene como efecto un
importante aumento del límite elástico y de la resistencia. Así, el material reforzado
presenta un límite elástico cercano a 1.300 MPa, a temperatura ambiente, frente a los 800
MPa que presenta el material sin reforzar, a la misma temperatura. En relación con las
propiedades mecánicas de los materiales tratados térmicamente, se observa que ambos
experimentan un acusado descenso de la ductilidad y de la resistencia máxima a la tracción. [EN] The mechanical properties of NI3Al-Cr reinforced with 10% in volume fraction of chromium particles produced by powder metallurgy have been studied. For this purpose, milled powders with composition of Ni-20.9Al-8Cr-0.49B (% at.) with and without the addition of 10% in volume fraction of chromium particles have been produced. Both alloys were consolidated by hot isostatic pressing (HIP). After HIP, heat treatment was applied to homogenize the microstructure. The chromium reinforcement has an important effect in the yield strength and ultimate strength increase. The reinforced alloy presents a yield strength of 1300 MPa at room temperature with respect to 800 MPa for the un-reinforced material. After heat treatment, the yield strength of both alloys does not change significantly. However, a decrease in ductility and ultimate tensile strength have been observed. |
Descripción: | 6 páginas, 9 figuras. | Versión del editor: | http://dx.doi.org/10.3989/revmetalm.2005.v41.i4.216 | URI: | http://hdl.handle.net/10261/21201 | DOI: | 10.3989/revmetalm.2005.v41.i4.216 | ISSN: | 0034-8570 | E-ISSN: | 1988-4222 |
Aparece en las colecciones: | (CENIM) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
214.pdf | 423,78 kB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
1
checked on 09-mar-2024
WEB OF SCIENCETM
Citations
3
checked on 24-feb-2024
Page view(s)
328
checked on 27-mar-2024
Download(s)
190
checked on 27-mar-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.