Title

Efecto de las variables de molienda en las propiedades de aleaciones Cu-NbC obtenidas por pulvimetalurgia

Other TitlesEffect of milling conditions on the properties of Cu-NbC alloys obtained by powder metallurgy
AuthorsLópez Valero, Manuela; Jiménez, José Antonio CSIC ORCID CVN ; Ruano, Oscar Antonio CSIC ORCID; Benavente, R.
KeywordsReforzamiento materiales compuestos base cobre
Pulvimetalurgia
Propiedades mecánicas y eléctricas
Strengthening of copper composite materials
Powder metallurgy
Mechanical and electrical properties
Issue Date30-Oct-2006
PublisherConsejo Superior de Investigaciones Científicas (España)
CitationRevista de Metalurgia 42(5): 324-333 (2006)
Abstract[ES] En este trabajo se han preparado materiales compuestos base cobre, reforzados con una dispersión homogénea de 0,5 y 1% (vol.) de partículas muy finas de carburo de niobio, mediante el proceso de molienda mecánica durante 8 y 24 h y utilizando velocidades de rotación de 153 y 300 rpm. La consolidación de las partículas reforzadas obtenidas, se realizó mediante compactación uniaxial aplicando una presión de 90 MPa en caliente a 923K durante 2 h, bajo atmósfera protectora de argón. La adecuada combinación de propiedades obtenidas en esta aleación, conductividad eléctrica y propiedades mecánicas, frente a otras aleaciones base cobre similares estudiadas, se debe a la dureza y suficiente estabilidad térmica del carburo de niobio que provoca un mayor refinamiento del tamaño de partícula de cobre con un reforzamiento de la aleación. Se observó una menor fragilización y mayor conductividad eléctrica de esta aleación, como consecuencia de la menor cantidad de impurezas (hierro, cromo, carbono y oxígeno) incorporadas durante la molienda de baja energía. Mediante microscopía electrónica de barrido, de transmisión y difracción de rayos X se demuestra, además, que se produce un reforzamiento microestructural adicional por la precipitación de las impurezas nanométricas.
[EN] Copper-base composite materials were obtained by reinforcing with homogeneous dispersions of 0.5 and 1% vol. of very fine NbC particles, through mechanical milling process in a planetary mill during 8 and 24 h at two different rotational speeds. The consolidation of the alloyed reinforced particles was achieved through a hot uniaxial pressing at 923K under 90 MPa during 2 h under a protective argon atmosphere. Factors to the suitable combination of electrical conductivity and mechanical properties attained are the hardness and good thermal stability of the niobium carbide which affords further refinement in the size of copper particles and the reinforcement of the alloy. A lower embrittlement and higher electrical conductivity of this alloy was observed, as a consequence of the smaller amount of impurities (Fe, Cr, C and O) incorporated during the lower-energy milling. Scanning and transmission electron microscopy and X-ray diffraction show an additional strengthening of the grain substructure by precipitation of nanometer-size impurities.
Description10 páginas, 2 tablas, 8 figuras.
Publisher version (URL)http://dx.doi.org/10.3989/revmetalm.2006.v42.i5.30
URIhttp://hdl.handle.net/10261/21152
DOI10.3989/revmetalm.2006.v42.i5.30
ISSN0034-8570
E-ISSN1988-4222
Appears in Collections:(CENIM) Artículos




Files in This Item:
File Description SizeFormat
107.pdf2,87 MBAdobe PDFThumbnail
View/Open
Show full item record
Review this work

SCOPUSTM   
Citations

1
checked on Jun 26, 2022

Page view(s)

522
checked on Jul 3, 2022

Download(s)

222
checked on Jul 3, 2022

Google ScholarTM

Check

Altmetric

Dimensions


WARNING: Items in Digital.CSIC are protected by copyright, with all rights reserved, unless otherwise indicated.