Title

Effect of the heating rate on the microstructure of a ferritic ODS steel with four oxide formers (Y-Ti-Al-Zr) consolidated by spark plasma sintering (SPS)

AuthorsMacía, Eric; García-Junceda, Andrea; Serrano, Marta; Hernández-Mayoral, M.; Díaz, Luis A. ; Campos, Mónica
KeywordsODS steel
Mechanical alloying
Spark plasma sintering (SPS)
Yield strength model
Issue Date2019
PublisherElsevier
CitationJournal of Nuclear Materials 518: 190-201 (2019)
AbstractThe proposed ODS ferritic steel alloyed with (Y-Ti-Zr-Al) was produced by mechanical alloying (MA) and spark plasma sintering (SPS) to obtain a complex nanostructure. To densify the material, a sintering cycle by SPS was performed at 1100 °C using fast heating rates (from 100 to 600 °C/min). During the attrition of MA powders, the uneven distribution of deformation level and of alloying elements has produced an inhomogeneous recrystallization during the consolidation step. Influence of processing condition was studied by modifying the heating rate of SPS to promote a heterogeneous material with bimodal grain size distribution. The final microstructures were characterized by X-ray diffraction and electron microscopy (SEM and TEM). The mechanical behaviour at R.T. was characterized by means of the Vickers microhardness and micro tensile tests. The good balance obtained between ductility (∼22–26%) and yield stress (800–910 MPa) at room temperature is provided by the bimodal grain size distribution. To predict the experimental values depending on the processing conditions, a yield strength model is presented. This model covers the contribution of different strengthening mechanism from solid solution, grain size, dislocation density and oxides precipitation. The model indicates the dislocation density as the major strengthening contribution. In addition, small punch (SP) tests were performed to analyse the response of the material at high temperatures where remarkable properties have been achieved.
Publisher version (URL)https://doi.org/10.1016/j.jnucmat.2019.02.043
URIhttp://hdl.handle.net/10261/201737
DOI10.1016/j.jnucmat.2019.02.043
ISSN0022-3115
Appears in Collections:(CINN) Artículos
Files in This Item:
File Description SizeFormat 
accesoRestringido.pdf59,24 kBAdobe PDFThumbnail
View/Open
Show full item record
Review this work
 

Related articles:


WARNING: Items in Digital.CSIC are protected by copyright, with all rights reserved, unless otherwise indicated.