Thermal properties and crystallization of iron phosphate glasses containing up to 25 wt% additions of Si-, Al-, Na- and U-oxides

AuthorsRusso, Diego O.; Rodríguez, Diego S.; Rincón López, Jesús María; Romero, Maximina; González Oliver, Carlos J. R.
KeywordsChemical durability
X-ray diffraction
Glass melting
Glass formation
Glass transition
SEM S100
Thermal properties
Issue Date1-Mar-2008
CitationJournal of Non-Crystalline Solids 354(14): 1541-1548(2008)
AbstractThe thermal properties (expansion, Tg and TSOFT.) of glasses, having 56–66% P2O5, 14.8–34.2% Fe2O3 and 2–25 wt% additions of SiO2, Al2O3, Na2O and UO2, were comparatively estimated from dilatometric measurements in similar conditions. The Tg reversibility was clearly verified by varying the heating rates between 1 and 5 °C min−1. From linear equations fits of the various glass properties as functions of the six components it is suggested the iron, sodium and uranium oxides decrease the thermal expansion (for 50 < T less-than-or-equals, slant 300 °C), Tg and TSOFT. From DTA/XRD analysis of three glasses it was confirmed the crystallization tendency decreased with increasing the UO2 level in the glasses. Leaching test data for two compositions containing Na2O suggest addition of UO2 increases the chemical durability of the related glass. The roles of UO2, Na2O and Fe-oxide species as structural components of the glass network are discussed.
Publisher version (URL)http://dx.doi.org/10.1016/j.jnoncrysol.2007.08.044
Appears in Collections:(IETCC) Artículos
Files in This Item:
There are no files associated with this item.
Show full item record
Review this work

Related articles:

WARNING: Items in Digital.CSIC are protected by copyright, with all rights reserved, unless otherwise indicated.