Título: | Structure, chemical durability and crystallization behavior of incinerator-based glassy systems |
Autor: | Barbieri, L.; Karamanov, A.; Corradi, A.; Lancellotti, I.; Pelino, M.; Rincón López, Jesús María CSIC ORCID | Palabras clave: | Chemical durability Crystallization Glass-ceramics ; Glasses ; Silicates ; X-ray diffraction |
Fecha de publicación: | 15-ene-2008 | Editor: | Elsevier | Citación: | Journal of Non-Crystalline Solids 354(2-9): 521-528 (2008) | Resumen: | Vitrification by melting is being proposed as a convenient method to solidify different kinds of silicate and other oxide-based inorganic wastes. Incinerator bottom and fly ashes have been mixed with glass cullet, feldspar and clay by-products as melting fluxing agents. Washing, drying, and grinding pre-treatments followed by melting at 1450 °C lead to the formation of glasses and glass-ceramics, depending on the starting materials composition and thermal treatment. The obtained glasses have been studied by SEM, chemical durability tests in aqueous and alkaline environment, leaching test (UNI 10802), and by differential thermal analysis. The glass-ceramics morphology was investigated by XRD and SEM. The results were explained by the structure of the glasses caused by the presence of different amount of modifiers in the glassy lattice. The obtained glasses show good chemical resistance, in particular in alkaline environment and thermal characterization highlighted that the materials are also suitable to obtain glass-ceramics. | Versión del editor: | http://dx.doi.org/10.1016/j.jnoncrysol.2007.07.080 | URI: | http://hdl.handle.net/10261/19949 | DOI: | 10.1016/j.jnoncrysol.2007.07.080 | ISSN: | 0022-3093 |
Aparece en las colecciones: | (IETCC) Artículos |
Mostrar el registro completo
CORE Recommender
SCOPUSTM
Citations
36
checked on 10-abr-2024
WEB OF SCIENCETM
Citations
33
checked on 26-feb-2024
Page view(s)
363
checked on 18-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.