Title

Effect of the synthesis conditions on the properties of La0.15Sm0.35Sr0.08Ba0.42FeO3 − δ cathode material for SOFCs

AuthorsVidal, Karmele; Larrañaga, Aitor; Morán-Ruiz, Aroa; Laguna-Bercero, M. A.; Baker, R. T.; Arriortua, María Isabel
KeywordsChemical synthesis
Oxygen content
SOFC
Cathode material
Impedance spectroscopy
Issue Date2017
PublisherElsevier
CitationPowder Technology 322: 131-139 (2017)
AbstractThe perovskite La0.15Sm0.35Sr0.08Ba0.42FeO3 − δ has been prepared by the glycine nitrate (GNC) route, varying the fuel/oxidizer ratio (glycine/nitrate, G/N = 1 and 2) and cooling rate (slow cooling and air-quenched), in order to study the influence of sample preparation on the materials' properties, in the context of their application as a cathode material for SOFCs. For this, the performance of the prepared mixed ion and electron conducting perovskite oxides is dictated by their structure, oxygen stoichiometry (3 − δ), chemical composition and thermal expansion properties. High-resolution Synchrotron X-ray powder diffraction patterns were collected at room temperature and at 700 and 800 °C. It was found that the materials had a cubic crystal structure at these temperatures. As expected, 3 − δ decreased as temperature increased, and was slightly smaller for the quenched sample. Higher electrical conductivity values were obtained for the sample with G/N = 1 (air-quenched) in the cooling rate. At 700 and 800 °C the cathode synthesized with G/N = 1 and air-quenched showed the smallest polarization resistance values in impedance spectroscopy studies. Therefore, the physicochemical and electrochemical characterization clearly demonstrated the influence of the synthetic conditions on the cathode performance.
Publisher version (URL)https://doi.org/10.1016/j.powtec.2017.09.020
URIhttp://hdl.handle.net/10261/181920
DOI10.1016/j.powtec.2017.09.020
ISSN0032-5910
E-ISSN1873-328X
Appears in Collections:(ICMA) Artículos
Files in This Item:
File Description SizeFormat 
effectSOFC.pdf205,67 kBAdobe PDFThumbnail
View/Open
Show full item record
Review this work
 

Related articles:


WARNING: Items in Digital.CSIC are protected by copyright, with all rights reserved, unless otherwise indicated.