Título

Effect of Na substitution and Ag addition on the superconducting properties of Bi-2212 textured materials

AutorÖzçelik, Bekir; Nane, O.; Sotelo, Andres CSIC ORCID; Amaveda, H. CSIC ORCID; Madre, M. A. CSIC ORCID
Fecha de publicación2017
EditorSpringer Nature
CitaciónJournal of Materials Science: Materials in Electronics 28(8): 6278-6283 (2017)
ResumenThe effect of Ag addition on the structural and superconducting properties of Bi2Sr2Ca0.925Na0.075Cu2Oy + x wt% Ag materials with x = 0, 1, 3, and 5 prepared by sol–gel method, followed by directional growth using the laser floating zone (LFZ) technique has been investigated. Powder XRD measurements demonstrate that all samples are composed by nearly single Bi-2212 phase. SEM micrographs and EDX results confirms that Bi-2212 is the major phase with minor amounts of a Bi-free one (Sr,Ca)CuO2 and metallic Ag. According to the magnetic results, Ag does not modify the superconducting critical temperature, T c , but significantly increases the magnetic hysteresis loop area. The magnetic critical current density is maximum in the 3 wt% Ag containing samples, due to the larger grain clusters found in these samples, reaching 2.1 × 105 A/cm2 at 10 K. Moreover, Ag addition also improves the rods mechanical properties, determined by three point bending tests. The highest bending stress is also reached in the 3 wt% Ag samples.
Versión del editorhttps://doi.org/10.1007/s10854-016-6309-0
URIhttp://hdl.handle.net/10261/181906
DOI10.1007/s10854-016-6309-0
ISSN0957-4522
E-ISSN1573-482X
Aparece en las colecciones: (ICMA) Artículos




Ficheros en este ítem:
Fichero Descripción Tamaño Formato
effectAgBi.pdf1,55 MBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo

CORE Recommender

SCOPUSTM   
Citations

8
checked on 21-mar-2024

WEB OF SCIENCETM
Citations

9
checked on 17-feb-2024

Page view(s)

205
checked on 28-mar-2024

Download(s)

121
checked on 28-mar-2024

Google ScholarTM

Check

Altmetric

Altmetric


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.