Título: | Structural properties of charge disproportionation and magnetic order in Sr2/3Ln1/3FeO3 (Ln=La, Pr, and Nd) |
Autor: | Blasco, Javier CSIC ORCID; Rodríguez-Velamazán, J. A. CSIC ORCID; García, Joaquín CSIC ORCID; Subías, G. CSIC ORCID; Piquer, Cristina CSIC; Cuartero, Vera CSIC ORCID; Sánchez, María Concepción CSIC ORCID; Stankiewicz, Jolanta CSIC ORCID | Fecha de publicación: | 2018 | Editor: | American Physical Society | Citación: | Physical Review B 98(1): 104422 (2018) | Resumen: | The structural properties and the magnetic ground state of Sr2/3Ln1/3FeO3 (Ln = La, Pr, Nd) samples were studied by means of synchrotron x-ray powder diffraction, neutron powder diffraction, and Mössbauer spectroscopy. All samples exhibit a metal-insulator-like transition coupled to a magnetic arrangement at a critical temperature, TMI. The diffraction techniques reveal strong structural changes at TMI that lead to new cells with reduced symmetry at low temperature. The new symmetry of the low-temperature phase has been determined for all compounds. The space groups are P¯3c1 for La-based compound and A2/n for the rest of samples. The high-resolution x-ray patterns detected superstructure peaks that can be accounted for by a small charge disproportionation between two nonequivalent Fe sites in the low-temperature phase explained in terms of a charge density wave that propagates along one of the body diagonals of the primitive cubic cell of these compounds. Our results clearly reveal that a full charge disproportionation of Fe4+ into Fe3+ and Fe5+ is not produced. We have determined the magnetic ordering of these samples exhibiting an antiferromagnetic structure with a sixfold periodicity with respect to the primitive cubic structure. The magnetic group accounting for the magnetic arrangements was obtained by a symmetry analysis and it is C2/c (15.85) for all samples but with different unit cell depending on the type of FeO6 tilts. The collinear ordering of Fe moments is established perpendicular to the charge density wave (along the body diagonal of the primitive cubic cell) and also perpendicular to the unique monoclinic axis. | URI: | http://hdl.handle.net/10261/181376 | DOI: | 10.1103/PhysRevB.98.104422 | ISSN: | 2469-9950 | E-ISSN: | 2469-9969 |
Aparece en las colecciones: | (ICMA) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
SrLnFeO.pdf | 3,08 MB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
12
checked on 19-abr-2024
WEB OF SCIENCETM
Citations
11
checked on 22-feb-2024
Page view(s)
205
checked on 21-abr-2024
Download(s)
241
checked on 21-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
Este item está licenciado bajo una Licencia Creative Commons