Título: | Effect of Na-doping on thermoelectric and magnetic performances of textured Bi2Sr2Co2Oy ceramics |
Autor: | Çetin, Gize; Özçelik, Bekir; Torres, M. A. CSIC ORCID ; Madre, M. A. CSIC ORCID; Sotelo, Andres CSIC ORCID | Palabras clave: | Thermoelectrics Laser processing Seebeck coefficient Power factor Figure of merit |
Fecha de publicación: | 2018 | Editor: | Elsevier | Citación: | Journal of the European Ceramic Society 38(2): 515-520 (2018) | Resumen: | Bi2Sr2-xNaxCo2Ox (x = 0.0, 0.025, 0.050, 0.075, 0.100, and 0.125) samples were prepared through the solid-state route and textured using the laser floating zone technique. Microstructural analysis of as-grown samples showed well oriented grains and a relatively high amount of secondary phases due to their incongruent melting. Annealing procedure has drastically decreased the number and amount of secondary phases. Moreover, Na-doping has further decreased the secondary phases content and improved grain alignment. These modifications have been reflected in a large decrease of electrical resistivity with the annealing procedure. The maximum power factor values have been obtained in 0.075 Na-doped annealed samples, 0.20 mW/K2m, which are much higher than the best values obtained in textured materials through hot uniaxial pressing. Magnetic properties were very similar for all samples, with paramagnetic Curie temperature and effective magnetic moment values of −48.6 K and ≈2 μB, respectively. | Versión del editor: | https://doi.org/10.1016/j.jeurceramsoc.2017.09.006 | URI: | http://hdl.handle.net/10261/180961 | DOI: | 10.1016/j.jeurceramsoc.2017.09.006 | ISSN: | 0955-2219 | E-ISSN: | 1873-619X |
Aparece en las colecciones: | (ICMA) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
manuscript_180961.pdf | 539,45 kB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
17
checked on 18-abr-2024
WEB OF SCIENCETM
Citations
15
checked on 22-feb-2024
Page view(s)
233
checked on 20-abr-2024
Download(s)
199
checked on 20-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.