Título: | Transparent Sol-Gel Oxyfluoride Glass-Ceramics with High Crystalline Fraction and Study of RE Incorporation |
Autor: | Gorni, Giulio; Velázquez, J. J.; Mosa Ruiz, Jadra CSIC ORCID; Mather, Glenn C. CSIC ORCID; Serrano Rubio, Aída CSIC ORCID ; Vila, María; Castro, Germán R. CSIC ORCID ; Bravo, David; Balda, Rolindes CSIC ORCID; Fernández, Joaquín CSIC ORCID; Durán, Alicia CSIC ORCID ; Castro Martín, Yolanda CSIC ORCID | Palabras clave: | Glass-ceramic Oxyfluoride Rare-earth Crystallization Sol-gel |
Fecha de publicación: | 3-abr-2019 | Editor: | Multidisciplinary Digital Publishing Institute | Citación: | Nanomaterials 9(4): 530 (2019) | Resumen: | Transparent oxyfluoride glass-ceramic films and self-supported layers with composition 80SiO<sub>2</sub>-20LaF<sub>3</sub> doped with Er<sup>3+</sup> have been successfully synthesized by sol-gel process for the first time. Crack-free films and self-supported layer with a maximum thickness up to 1.4 µm were obtained after heat treatment at the low temperature of 550 °C for 1 min, resulting in a LaF<sub>3</sub> crystal fraction of 18 wt%, as confirmed by quantitative Rietveld refinement. This is the highest value reported up to now for transparent oxyfluoride glass-ceramics prepared by sol-gel. This work provides a new synthesis strategy and opens the way to a wide range of potential applications of oxyfluoride glass-ceramics. The characterization by a wide range of techniques revealed the homogeneous precipitation of LaF<sub>3</sub> nanocrystals into the glass matrix. X-ray absorption spectroscopy and electron paramagnetic resonance confirmed that the Er<sup>3+</sup> ions are preferentially embedded in the low phonon-energy LaF<sub>3</sub> nanocrystals. Moreover, photoluminescence (PL) measurements confirmed the incorporation of dopants in the LaF<sub>3</sub> nanocrystals. The effective concentration of rare-earth ions in the LaF<sub>3</sub> nanocrystals is also estimated by X-ray absorption spectroscopy. | Versión del editor: | http://dx.doi.org/10.3390/nano9040530 | URI: | http://hdl.handle.net/10261/180713 | DOI: | 10.3390/nano9040530 | ISSN: | 2079-4991 |
Aparece en las colecciones: | (ICMM) Artículos (CFM) Artículos (ICV) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
nanomaterials-09-00530.pdf | 3,17 MB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
PubMed Central
Citations
9
checked on 17-mar-2024
SCOPUSTM
Citations
22
checked on 15-abr-2024
WEB OF SCIENCETM
Citations
18
checked on 25-feb-2024
Page view(s)
341
checked on 17-abr-2024
Download(s)
218
checked on 17-abr-2024