Título

Up-Conversion emission in Er-Yb doped transparent oxy uoride nano-glass-ceramics

AutorGorni, Giulio; Balda, Rolindes CSIC ORCID; Fernández, Joaquín CSIC ORCID; Velázquez, J. J.; Pascual, Laura CSIC ORCID ; Durán, Alicia CSIC ORCID ; Pascual, M. Jesús CSIC ORCID
Palabras claveTransparent glassceramics
Fluorides
Optical properties
Fecha de publicación2018
CitaciónPNCS-ESG 2018
ResumenOxyfluoride glass-ceramics have become increasingly important in the last decades because they combine the advantages of glass processing with the good crystalline properties, such as good mechanical, thermal and optical ones. From the pioneering work of Wang and Ohwaki in 1993, concerning the e cient green and red Up-Conversion (UC) emission in Er3+-Yb3+ doped GCs containing PbxCd1-xF2 nano-crystals (NCs), many fluoride crystal phases have been studied, showing the possibility to e ectively improve the luminescence of Rare-Earth ions (REI) when they are embedded in fluoride NCs. LnF3 [2] or RLnF4 [3] (R= K, Na, Li) crystals phases are especially important because the similar size of ions crystals former and the other REI used as dopants allows their incorporation into the crystals phase. In these work, two oxyfluoride compositions doped with 0.5Er and co-doped with 2 and 4Yb (mol %) have been studied. A structural study, performed by XRD, showed the precipitation of LaF3 or NaGdF4 nano-crystals in the glass. HR-TEM and XANES techniques have allowed evidencing the Er3+ and Yb3+ enrichment in the nano-crystals and estimating their concentration in the crystal phase. Optical measurements of Er3+ singly doped and Yb3+ co-doped samples showed UC emission (green and red) upon NIR excitation at 980 nm. A notable improve in the UC emission intensity is observed from glasses to GCs and the two-photon origin of the process was proved. Moreover, the green/red ratio of the UC emission changes with the heat treatment of GCs and a possible explication related to the REI concentration is given.
DescripciónResumen del póster presentado al 15th International Conference on the Physics of Non-Crystalline Solids (PNCS) y a la 14th European Society of Glass Conference (ESG), celebradas en Saint Malo (Francia) del 9 al 13 de julio de 2018.
URIhttp://hdl.handle.net/10261/179528
Aparece en las colecciones: (CFM) Comunicaciones congresos
(ICV) Comunicaciones congresos
(ICP) Comunicaciones congresos




Ficheros en este ítem:
Fichero Descripción Tamaño Formato
accesoRestringido.pdf59,24 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo

CORE Recommender

Page view(s)

225
checked on 29-mar-2024

Download(s)

36
checked on 29-mar-2024

Google ScholarTM

Check


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.