Título

Influence of hydrogen bubbles adhering to the exposed surface on the corrosion rate of magnesium alloys AZ31 and AZ61 in sodium chloride solution

AutorFeliú Jr., S.; García-Galván, F. R.; Llorente, Irene; Díaz, Iván; Simancas Peco, Joaquín
Palabras claveMagnesium alloys
Weight loss
XPS
Passivity
EIS
Fecha de publicación2017
EditorJohn Wiley & Sons
CitaciónMaterials and Corrosion - Werkstoffe und Korrosion 68 (6): 651-663 (2017)
ResumenThe influence of the presence of hydrogen bubbles adhered to the corroding specimen surface on the EIS estimations of corrosion rate of magnesium alloys is considered. The EIS corrosion rates for AZ31 specimens exposing a small area were four times higher than the real values determined by gravimetric or hydrogen evolution measurements. In contrast, no significant differences in the corrosion rate have been observed in the case of the AZ61 specimens. A progressive deterioration in the protective properties of the corrosion products layer formed during the test was observed only on AZ31 specimens exposing a small area.
Versión del editorhttps://doi.org/10.1002/maco.201609233
URIhttp://hdl.handle.net/10261/172325
Identificadoresdoi: 10.1002/maco.201609233
issn: 1521-4176
Aparece en las colecciones: (CENIM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
accesoRestringido.pdf15,38 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 

Artículos relacionados:


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.