Título

Influence of aluminium enrichment in the near-surface region of commercial twin-roll cast AZ31 alloys on their corrosion behaviour

AutorDelgado, M.C.; García-Galvan, F.R.; Llorente, Irene; Pérez Zubiaur, Pablo; Adeva, Paloma; Feliú Jr., S.
Palabras claveXPS
Passive films
EIS
SEM
Magnesium
Fecha de publicación2017
EditorElsevier
CitaciónCorrosion Science 123: 182-196 (2017)
ResumenThe effect of increasing the Al concentration to a value between 0.5 and 0.8 wt.% within the 10-μm thick surface layer of a commercial AZ31 alloy sheet manufactured by twin-cast rolling method on its corrosion behaviour was investigated. In long term exposure, both the uniformity of the double layered Mg-Al hydroxide (LDH) formed in the inner layer of the corrosion product on the aluminium-rich surface AZ31 specimen and the precipitation of a significant amount of aluminium hydroxide contributed to enhancing the corrosion resistance significantly.
Versión del editorhttps://doi.org/10.1016/j.corsci.2017.04.027
URIhttp://hdl.handle.net/10261/172189
Identificadoresdoi: 10.1016/j.corsci.2017.04.027
issn: 0010-938X
Aparece en las colecciones: (CENIM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
accesoRestringido.pdf15,38 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 

Artículos relacionados:


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.