Title

Effect of marine aerosols on the alteration of silicate glasses

AuthorsPalomar Sanz, Teresa ; Chabas, A.; Bastidas, David M.; Fuente, Daniel de la; Verney-Carron, A.
KeywordsGlass
Degradation
Aerosols
Sodium chloride
Issue Date1-Sep-2016
PublisherElsevier
CitationJournal of Non-Crystalline Solids 471: 328-337 (2016)
AbstractThis work is focused on the effect of marine aerosols on soda-lime, potash-lime and lead silicate glass samples. Two kinds of tests were carried out, the first one under laboratory controlled condition during 36 days to evaluate the alteration of glass surface by NaCl aerosols, and the second one in a marine atmosphere in Cabo Vilano (Galicia, Spain) for up to three months. Both tests showed similar results. NaCl aerosols acted as condensation nuclei in high humidity environments favoring the lixiviation of the alkaline and alkaline-earth ions from the glass surface and the solubilization of atmospheric gases (CO2, SO2). Marine aerosols could also accelerate the corrosion attack inducing the loss of the surface hydrogen bonds and the opening of the network accelerating the corrosion mechanism. Results also confirmed that high humidity favored the alteration of the glass surface and the formation of new crystalline phases. Soda-lime silicate and lead silicate glasses were the most durable ones, whereas potash-lime silicate glass presented a fissured alteration layer due to the hydrolytic attack of the surface. New crystalline phases including chlorides, carbonates and sulfates were detected on the glass surfaces which can be related to marine aerosols, environmental particles and the reaction of the cations lixiviated from the glass with the atmospheric gases.
Publisher version (URL)http://dx.doi.org/10.1016/j.jnoncrysol.2017.06.013
URIhttp://hdl.handle.net/10261/153944
DOI10.1016/j.jnoncrysol.2017.06.013
ISSN0022-3093
E-ISSN1873-4812
Appears in Collections:(CENIM) Artículos
Files in This Item:
File Description SizeFormat 
Palomar_Effect_ Journal of Non-Crystalline Solids_2017.pdf Embargoed until September 1, 2019Postprint1,57 MBAdobe PDFThumbnail
View/Open    Request a copy
silicate_glasses.pdfPreprint1,34 MBAdobe PDFThumbnail
View/Open
Show full item record
 

Related articles:


WARNING: Items in Digital.CSIC are protected by copyright, with all rights reserved, unless otherwise indicated.