Título: | High surface area stainless steel wire mesh-supported TiO2 prepared by sacrificial template accelerated hydrolysis. A monolithic photocatalyst superior to P25 TiO2 |
Autor: | Vu, Thi Tan CSIC ORCID; Valdés-Solís Iglesias, Teresa CSIC ORCID ; Marbán Calzón, Gregorio CSIC ORCID | Palabras clave: | TiO2 Sacrificial template Photodegradation Methylene blue P25 TiO2 |
Fecha de publicación: | oct-2014 | Editor: | Elsevier | Citación: | Journal of Environmental Chemical Engineering 2(4): 2229-2235 (2014) | Resumen: | High surface area stainless steel wire mesh-supported TiO2 catalysts were prepared by sacrificial template accelerated hydrolysis using highly polar stainless steel wire mesh-supported ZnO templates. The monolithic catalysts were tested for the photodegradation of methylene blue in aqueous solution under ultraviolet irradiation. The calcination temperature of the catalysts was observed to have a determinant effect on their catalytic activity. The optimum calcination temperature range was 450–600 °C, in which a combination of high surface area (50–90 m2 g−1), a high degree of crystallinity and a minimum rutile content yielded the best catalytic results, with maximum catalytic activity appearing for a calcination temperature of 450 °C. The most active catalyst prepared in this work displayed twice the catalytic activity of the reference catalyst, P25 TiO2. | Versión del editor: | http://dx.doi.org/10.1016/j.jece.2014.10.002 | URI: | http://hdl.handle.net/10261/111038 | DOI: | 10.1016/j.jece.2014.10.002 | ISSN: | 2213-3437 |
Aparece en las colecciones: | (INCAR) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
High_surface_Vu.pdf | 738,73 kB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
12
checked on 12-abr-2024
Page view(s)
372
checked on 22-abr-2024
Download(s)
343
checked on 22-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.