Low temperature red luminescence of a fluorinated Mn-doped zinc selenite
Royal Society of Chemistry (UK)
2013
artículo
Orive, Joseba
Balda, Rolindes
Fernández, Joaquín
Lezama, Luis
Arriortua, María I.
2013
M2(SeO3)F2 (M = Zn (1), Mn (2)) stoichiometric phases together with the Zn2-xMnx(SeO 3)F2 compound doped at various concentrations (x = 0.002-0.2) were synthesized by employing mild hydrothermal conditions. These compounds have been characterized by scanning electron microscopy (SEM), Rietveld refinement of the X-ray powder diffraction patterns, ICP-Q-MS, thermogravimetric and thermodiffractometric analyses, and IR, UV/vis and electron paramagnetic resonance (EPR) spectroscopies. Compounds 1 and 2 crystallize in the orthorhombic Pnma space group with lattice parameters: a = 7.27903(4), b = 10.05232(6) and c = 5.26954(3) Å for the zinc species and a = 7.50848(9), b = 10.3501(12) and c = 5.47697(6) Å for the manganese phase, with Z = 4. The crystal structures of these compounds are isotypic and are built up from a 3D framework constructed by (010) sheets of [MO 3F3] octahedra linked up by [SeO3] building units. Luminescence measurements of Mn2(SeO3)F2 were performed at different temperatures between 10 and 150 K. At 10 K, the emission spectrum consists of a broad band peaked at around 660 nm related to the 4T1g → 6A1g transition in octahedrically coordinated Mn2+. Moreover, the influence of temperatures up to 295 K and the Mn concentration on the luminescent properties of the Zn2-xMnx(SeO3)F2 system were systematically studied. Magnetic measurements of 2 show antiferromagnetic coupling as the major interactions exhibiting a spin canting at low temperature. © 2013 The Royal Society of Chemistry.
Ministerio de Ciencia e Innovación (España)
Eusko Jaurlaritza
Universidad del País Vasco
Ministerio de Educación y Ciencia (España)
European Commission
Dalton Transactions
2013
42
12481
12494